EZ-Lam Tooling Resin - High Temperature

(0) No Reviews yet
$107.80 to $261.80
SKU: ET-TOOLING-RESIN-HT

Details

Description

EZ-Lam High Temperature Epoxy Resin is a two part, high temperature curing laminating system specially formulated for construction of high strength, high temperature composite parts. Its low viscosity offers excellent wet out characteristics and it is bondable to all fabrics including, fiberglass, carbon fiber, aramid (Kevlar®), core materials, wood and metal.

When combined, the mixture provides a pot life of four hours at 75°F. The resin must undergo room temperature set for 24-48 hours at 75°F, followed by a tiered post cure cycle, starting at 150°F and ending at 350°F. Allow the part to cool in the oven prior to removal. The maximum operating temperature is 450 °F.

The resulting laminate will cure to a hard, high strength gloss finish that can be easily sanded.

  • Available Sizes: Quart, Gallon
  • Shipping: Domestic Shipping via Ground Only

KEVLAR® is a registered trademark of E.I. du Pont de Nemours and Company and is used with permission.

Technical

Physical Properties
Mix Ratio:
Weight: 100 parts A to 30 parts B
Pot Life:
150 gr. mass 15 minutes @ 75°F
Cure:
  • Room Temp Set 24-48 Hours @ 75°F followed by:
  • 4 Hrs. @ 150°F
  • 2 Hrs. @ 200°F
  • 2 Hrs. @ 250°F
  • 2 Hrs. @ 300°F and allow to cool
Gel Time:
3-4 Hours
Shelf Life:
Twelve months when stored in tightly sealed containers at room temperature.
Color:
Amber
Technical Properties
Viscosity, Mixed:
3000 CPS
Durometer D:
90 Shore
Specific Gravity:
1.55 gm/cc
Tensile Strength:
45,000 psi
Flexural Modulus:
65,000 psi
Compression:
52,000 psi
Max Temperature:
300°F
Shrinkage
Less than 1%

Please note: All data to be used as a guide only; not a specification.