8.8 oz Fiberglass 8-Harness Satin Weave RTS Prepreg

(0) No Reviews yet
$49.50
QuantityPrice
1 - 4$49.50
5 - 9$44.00
10 - 49$37.40
50 - 99$33.00
100 +$30.80
SKU: PP-W-FG-8.8-8HS-50-P

Details

Description

Our Fiberglass Room Temperature Prepreg is an 8.8 oz 8 Harness Satin Weave E-Glass fabric impregnated with a thermosetting epoxy resin system. It can be stored at room temperatures and does not require freezer storage. With the long out life of the resin matrix, the fiberglass prepreg can be shipped and processed at room temperatures. It is ideal for use when a long shelf life is desired, high-temperature capabilities are not required and controlled resin content is wanted.

The 8 Harness is a highly pliable fabric is ideal for applications with compound curves. The unique epoxy resin system allows for various flexible cure cycles and has a long out-life.

Please allow extra order processing time when order prepreg fabrics.

Technical

Physical Properties
Style:
7781
Weave:
8 Harness Satin Weave
Weight:
8.81 oz/yd²
Thickness:
.008"
Fabric Count (Warp x Fill):
57 x 54
Fiber Type:
E-Glass
Resin Matrix:
Epoxy
Resin Content:
30% by Weight
Technical Resin Properties*
Density:
1.22 g/cc
Tensile Strength:
76.5 MPa / 11.1 kpsi
Tensile Modulus:
10.7 GPa / 427 kpsi
Strain (% Elongation) :
3.75%
DMA - Dry Glass Transition
Glass Transition – E" Peak:
132°C / 270°F
Glass Transition – E' Onset:
130°C / 265°F
Glass Transition – Tan δ Peak:
146°C / 295°F
DMA – Wet Glass Transition**
Glass Transition – E" Peak:
86°C / 187°F
Glass Transition – E' Onset:
81°C / 179°F
Glass Transition – Tan δ Peak:
98°C / 208°F
Water Abbsorbtion**:
3.8%
Composite Properties***
0° Tensile Strength:
0.75 GPa / 110 kpsi
0° Tensile Modulus:
76 GPa / 11 Mpsi
0° Tensile Percent Strain:
1.0 %
0° Tensile Poisson’s Ratio:
0.20
0° Compressive Strength:
0.62 GPa / 9.0 x 101 kpsi
0° Compression Modulus:
52 GPa / 7.5 Mpsi
Short Beam Strength:
63 MPa / 9.1 kpsi
Flexural Strength:
0.74 GPa / 108 kpsi
Cure Cycles
Option 1
≤ 5°F-per-minute ramp up to 310°F (154°C), hold for 1 hour.
< 5°F-per-minute ramp down to at least 150°F (66°C) before removing from oven.
Option 2
≤ 5°F-per-minute ramp up to 290°F (143°C), hold for 2 hours.
< 5°F-per-minute ramp down to at least 150°F (66°C) before removing from oven.
Option 3
≤ 5°F-per-minute ramp up to 270°F (132°C), hold for 4 hours.
< 5°F-per-minute ramp down to at least 150°F (66°C) before removing from oven.
Shelf Life/Storage

Material should remain sealed when not is use and stored indoors, out of the weather.

  • 6 months from date of manufacture when the maximum temperature storage does not exceed 90°F(32°C)
  • 12 months from date of manufacture when the maximum temperature storage does not exceed 75°F(24°C)
  • 30 months from date of manufacture when the maximum temperature storage does not exceed 0°F(-18°C), with an additonal 6 months at <75°F (24°C).

Please note: All data to be used as a guide only; not a specification. *Cure cycle: 1 hour at 154°C **DMA wet glass transition and water absorption measured after 24-hour water boil ***Reinforcement: T300-3K 2x2 twill 50” carbon fiber fabric. Composite properties are express to two significant figures. Cure cycle: 4 hours at 132°C (270°F), via vacuum bag oven cure, tests conducted at 22°C (72°F)