2.95 oz. Blue Carbon Fiber Spread Tow - TeXtreme® 1000

(0) No Reviews yet
1 - 4$153.10
5 - 9$150.04
10 - 24$146.98
25 - 49$143.91
50 - 99$140.85
100 +$137.79
SKU: XS-W-CF-2.95-ST-39-PRO-P



TeXtreme®'s Spread Tow fabric (STF) is a unique fabric that increases performance as well as reduces laminate weight up to 20%. TeXtreme® 1000 utilizes a 15K/50 gsm/20mm wide unidirectional tape to produce a fabric with a fiber weight of 2.95 oz/yd2. The woven fabric is stabilized with an epoxy compatible binder that is 0.29 oz/yd2 (10gsm) to hold the material together and to allow for easy cuts, trimming or slitting with clean edges and no fraying. The weight of the fabric does not include the weight of the binder and should be considered when determining in the amount of epoxy needed for a laminate.

What makes this fabric different that traditional woven fabrics is TeXtreme®'s proprietary spreading technology. Traditionally, the tow used to weave composite fabrics is round or oblong in nature. This presents challenges when trying to achieve low aerial weights and has shown lower mechanical properties of a fabric because of inherent crimp or waviness that is being introduced in the fibers.

As an example, a typical 200 gsm 3K Plain Weave 50” wide fabric will have about 23,000 places where the weave overlaps, also called a crimp. Each crimp in the fabric has a very small area where excess resin will accumulate. By spreading the tow, the number of crimps is eliminated by over 90% which in turns eliminates the amount of area where excess resin can accumulate. In one yard of fabric you reduce over 21,000 of these super small resin pools yielding a part that is almost 20% lighter than a standard laminate.

Colored with Hypetex®’s patented coloring technologies, the Prost Spread Tow showcases a vibrant blue color, Pantone – 288c. Hypetex® uses water based resins and nano pigments that puts color onto the composite at the point of production, removing the need for expensive paints or coatings. The result is a colorful premium aesthetic part straight from the mold, reducing post processing costs and offering a more environmentally friendly coloring solution. Hypetex® coloring technologies are optimized for either thermoset or thermoplastic matrix systems and are mechanically characterized to aid structural optimization.

  • Achieve thinner laminates
  • Reduce weight by 20% or more
  • Desirable appearance
  • Smooth and low porous surface finish
  • Easy to handle, cut and place
Uses Include
  • Formula One & NASCAR Sprint Cup Racing
  • Cryonic tanks, aircraft interior components or UAVs
  • Hockey sticks and golf shafts
  • Thin ply carbon diaphragms


Physical Properties
Fiber Weight:
2.95 oz/yd² (100 gsm) +/- 3%
NM688, One Side
Binder/Stabilizer Weight:
0.29 oz/yd² (10 gsm) +/- 3g/m²
Epoxy Compatible
Fabric Count (Warp x Fill):
15 x 15
Warp Fiber:
HS Carbon Fiber 15K 50gsm
Fill Fiber:
HS Carbon Fiber 15K 50gsm
Tape Width:
Dry and Below 86° F
UV Sensitive:
Thickness of one ply laminate @60% VF::
Vendor Part:
TeXtreme® 1000
Technical Fiber Properties
HS Carbon Fiber 15K 50gsm
0.066 lb/in³
Tensile Strength:
710 ksi
Tensile Modulus:
34 msi

Please note: All data to be used as a guide only; not a specification.

Data Sheets
  • Epoxy Resin
  • Polyester Resin
  • Vinyl-ester Resin
  • For the best cosmetics, the side without the binder should be placed onto the mold surface.
  • The fabric is shipped with a plastic liner on one side to prevent the binder from sticking to the layer beneath it. The binder will start to soften at 65° F for improved processing at room temp.